Abstract
AbstractThree‐dimensional flow and structural analyses were carried out for film insert injection molding to investigate warpage of film insert molded (FIM) parts with respect to variation of film and substrate thickness. Asymmetry of temperature distribution in the thickness direction was increased with increasing film thickness but decreased with increasing substrate thickness. Asymmetry of the in‐mold residual stress distribution in the FIM specimen was generated by the nonuniform temperature distribution, and it was increased with increasing film thickness but reduced with increasing substrate thickness. Warpage of the ejected FIM specimen was determined by relaxation of the asymmetric in‐mold residual stress distribution, and it was increased with increasing film thickness but reduced with increasing substrate thickness. Warpage of FIM specimens annealed at 80°C for 30 min showed complex behavior, and the behavior was understood by using factors such as degree of warpage of the ejected part, thermal shrinkage of the inserted film, and retardation of heat transfer. POLYM. ENG. SCI., 2010. © 2010 Society of Plastics Engineers
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.