Abstract
Marine scrubbers use seawater as washing water and are damaged by sulfur oxides and chlorides during desulfurization. Therefore, surface treatments to enhance corrosion and pitting resistance of scrubber materials must be investigated. This investigation conducts cyclic potentiodynamic polarization experiments to analyze the effects of electropolishing and plasma ion nitiriding of UNS S31603 in washing water. The corrosion current density (0.186 μA cm-2) of electropolishing is significantly lower than mechanical polishing (1.125 μA cm-2), but plasma ion nitriding is higher (18.995 μA cm-2). Electropolishing forms a uniform and dense passivation film, increasing corrosion resistance, whereas plasma ion nitriding reduces corrosion resistance due to CrN formation. All specimens present local corrosion. Electropolishing reduces the maximum damage depth by 110.13 μm and increases pitting potential by 0.32 V compared to mechanical polishing. Plasma ion nitriding reduces maximum damage depth by 46.59 μm due to suppression of local acidification during hydrolysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.