Abstract
The effects of ground granulated blast furnace slag/fly ash (GGBFS/FA) ratio, mass ratio of SiO2 to Na2O (Ms) of activator solution and sodium silicate dosage on structural build-up, flow properties and setting characteristics of alkali-activated cement (AAC) mixtures were investigated. The solid-like behavior becomes more dominant with increasing GGBFS/FA ratio. Ms value had significant effect on the structural build-up. Significantly higher initial storage modulus with a low increasing rate was observed for the Ms values lower than 0.8. However, for higher Ms values, a sudden increase in storage modulus was observed after negligible initial structuration. An increase in sodium silicate dosage caused a considerable delay in the abrupt increase in the structural formation. It was observed that flow curves of AAC fit the Herschel-Bulkley model with shear-thickening behavior. ICP-OES tests revealed the lower release of aluminum and calcium into the pore solution of GGBFS/FA mixtures with low Ms values.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.