Abstract
Effects of welding speed on the microstructure evolution in the stir zone (SZ) and mechanical properties of the friction stir welding (FSW) joints were studied by OM, XRD, SEM, TEM, EBSD and tensile testing. Compared with the base metal (BM), an obviously fine dynamic recrystallization (DRX) microstructure occurs in the SZ and the DRX grain size decreases from 5.6 to 4.4 μm with the increasing of welding speed. Fine DRX microstructure is mainly achieved by continuous dynamic recrystallization (CDRX) mechanism, strain induced boundary migration (SIBM) mechanism and particle stimulated nucleation (PSN) mechanism. Meanwhile, the geometric coalescence and the Burke−Turnbull mechanism are the main DRX grain growth mechanisms. Among all the welding speeds, the joint welded at rotation speed of 1500 r/min and welding speed of 75 mm/min has the greatest tensile properties, i.e. ultimate tensile strength (UTS) of (509±2) MPa, yield strength (YS) of (282±4) MPa, elongation (El) of (23±1)%, and the joint efficiency of 73%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.