Abstract
This study shows how treated filler loading influences the photopolymerization of a dimethacrylate comonomer mixture, regarding, in particular, shrinkage and inhibition under atmospheric oxygen, present in oral environment. Bis-GMA/TEGDMA (75/25 wt.%) resins were loaded with hybrid filler (Ba aluminosilicate glass and pyrogenic silica), treated with gamma-methacryloxy(propyl)trimethoxysilane, at 0-50 wt.% and light cured over a total of 30 s (45 mW/cm2). Degree of double-bond conversion (DC), obtained using FTIR, decreased with filler content. 1H MAS spectra (293-340 K) and STRAFI images (293 K) were obtained as a function of irradiation time and filler concentration. 1H signals of unreacted methacrylate groups were more intense for higher loaded resins and resonances from -CH2SiO2(OH) (T2) and -CH2SiO3- (T3) units, also observed by 29Si NMR, were resolved and suggest the presence of T2-resin bonds. 1D images show a reduction on polymerization contraction and reaction inhibition at the composite resin surface with filler loading. 2D resin images present a highly mobile surface layer, hence with lower DC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Medicine
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.