Abstract
Three-layer core/shell latex particles with various shell crosslinking level and shell thickness were prepared by multistep emulsion polymerization, and the hollow latex particles with different morphologies were then obtained after alkali post-treatment. Influences of divinyl benzene (DVB) content and the core/shell mass ratio on emulsion polymerization and particle morphology were investigated. Results showed that with the increase of DVB content, the percentage of total amount of -COOH on the particle surface and free in aqueous phase (PSF a) decreased, and the morphology of the post-treated particles underwent evolution from cracked, intact hollow to deficient swelling structure. Decreasing the core/shell mass ratio could not only make more carboxyl groups encapsulated by the shell, but also increase the shell resistance to the swelling of the core. The uniform hollow latex particles with intact morphology were obtained when the DVB content was 3.54 wt% and the core/shell mass ratio was 1/6.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.