Abstract
AbstractRotomolded containers for solvents and hydrocarbons require the use of high‐permeability resins such as polyamide (PA). The published studies with this material are very scarce. In this work, a commercial grade of PA11 was rotational‐molded using different processing temperatures and characterized with a range of techniques. The study aims at investigating the influence of the processing conditions on the microstructure and properties of molded parts. The results showed that the spherulitic morphology and the mechanical properties are affected by the processing temperature, the optimum processing range being between 220°C and 240°C. Overheating causes a decrease of the impact strength and a severe increase in the formation of pinholes at the outer surface due to polymer degradation and formation of volatile products. The thermo‐oxidation reactions occurring at the inner surface of the samples result in the formation of products that absorb in the UV and visible light regions and cause the microhardness and the melt viscosity of the material to increase. The extent and severity of the degradation at the inner surface may be easily assessed by fluorescence microscopy. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.