Cuprous oxide (Cu2O) and cupric oxide (CuO) particles were synthesized using a wet chemical surfactant free method at different synthesis temperatures from 25 °C to 60 °C. Morphology, size, and chemical composition of the prepared Cu2O particles were analyzed by FESEM, PXRD, and UV-vis. We discovered that the chemical composition of the Cu2O particles remained unaffected by the synthesis temperature. However, morphology and size of the particles showed a strong temperature dependency. This could be attributed to the temperature induced formation of CuO species from the copper hydroxide (Cu(OH)2) precursor which also functions as copper precursor for the Cu2O particle growth. The cupric oxide species was determined to be the main cause for the formation of micrometer sized particles, whereas with the Cu(OH)2 precursor species for the Cu2O particles nanocubes with smaller edge lengths as well as octahedrons were obtained.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.