Abstract
This study focuses on the effect of pin taper tool ratio on friction stir welding of aluminum AA7075. Two pieces of AA7075 alloy with thickness of 6 mm were friction stir welded by using conventional milling machine. The shoulder diameter used in this experiment is fix 18mm. The taper pin ratio used are varied at 6:6, 6:5, 6:4, 6:3, 6:2,and 6:1. The rotational speeds that were used in this study were 1000 rpm, 1200 rpm and 1400 rpm, respectively. The welding speeds used are 60 mm/min, 80 mm/min and 100 mm/min. Microstructure observation of welded area was studied by using optical microscope. To evaluate the mechanical properties of this specimen, tensile test was used in this study. Welded specimens using taper pin ratio 6:2 shows higher tensile strength compared to other taper pin ratio up to 197 MPa. Moreover, taper pin ratio 6:1 showed better tensile test compared to taper pin ratio above 6:3. The optimum parameters were found to be taper pin ratio 6:2 with 1000 rpm of rotational speed and 60mm/min welding speed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.