Abstract
Direct carbon fuel cells are promising power sources with their performance significantly depending on the electrooxidation activity of carbon fuel. The impurities in the carbon fuel may affect the anode reactions. Sulfur and some of its inorganic compounds (CaSO4, K2SO3, K2S, FeS2) were added in molten carbonate and their effect on graphite electrooxidation was investigated. Cyclic voltammograms of gold electrode with addition of these sulfur compounds showed CaSO4 was stable and other compounds were electrochemically oxidized to high valence state sulfur compounds at operating voltage range. Linear sweep voltammetry of graphite with addition of sulfur compounds exhibited enhanced current density compared to pure graphite electrooxidation. Chronoamperometry was carried out to examine steady-state test of graphite electrooxidation in presence of sulfur compounds and the results indicated the enhanced current densities were caused by improved Boudouard reaction for CaSO4 and sulfur electrooxidation for other compounds, respectively. These inorganic sulfur compounds had no impact on electrooxidation process of graphite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.