Effect of Substrate Temperature on CdTe Thin Film Property and Solar Cell Performance

Abstract

Vapor transport deposition is an excellent method for preparing large area CdTe thin films with high quality and uniformity. Polycrystalline CdTe thin films were deposited by home-made vapor transport deposition system (VTD). The effects of substrate temperature on the property of CdTe film and the performance of CdTe solar cell were investigated. CdTe thin films were characterized by scanning electron microscope (SEM), X-ray diffraction (XRD), UV-Vis spectrometer, and Hall Effect system. The results show that the CdTe thin films deposited by vapor transport deposition are cubic phase with a preferred orientation in (111) direction. The average grain size increases from 2 m to 6 m and the carrier concentration increases from 1.93×10 cm to 2.36×10 cm when the substrate temperature increases from 520 °C to 620 °C. This suggests that high substrate temperature can increase the carrier density significantly due to the suppressed defect recombination. The performance of CdTe thin film solar cells deposited at different substrate temperatures demonstrates that high substrate temperature (610°C) can greatly improve the efficiency, open circuit voltage and fill factor of the solar cells. But the substrate temperature higher than 610°C will reduce the spectral 142 无 机 材 料 学 报 第 31卷 response of the cells in long wavelength region, which results in the degradation of solar cell performance. The small-area CdTe thin film solar cell without back contact layer deposited at substrate temperature of 610°C obtains the best conversion efficiency of 11.2%.