Abstract
PurposeThis paper aims to investigate the influence of slurry concentration on the erosion behavior of AISI 5117 steel and high-chromium white cast iron by using a whirling-arm rig. In this study, the slurry erosion mechanism with particle concentration has been studied.Design/methodology/approachThe tests were carried out with particle concentrations in the range of 1-7 Wt.%, and the impact velocity of slurry stream was 15 m/s. Silica sand with a nominal size range of 500-710 µm was used as an erodent. The study revealed that the failure mode was independent of concentration.FindingsThe results showed that the erosion rate decreases with the increase in particle concentration and the variation in the reduction depends on the material. It was found that the variation of fractal dimension calculated from slope of linearized power spectral density of eroded surface image for different concentrations can be used to characterize the slurry erosion intensity in a similar manner to the erosion rate. It was also found that the variation of fractal dimension versus concentration of sand has a general trend that does not depend on magnification factor.Originality/valueUsing the gravitational measurement and image analysis, the variation of the wear with slurry concentration has been analyzed to investigate the implicated mechanisms of erosion during the process.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.