Abstract
The mullite bonded SiC porous ceramic products were prepared by pressing, molding, drying, pre sintering and sintering with alumina (Al2O3), silica (SiO2), carbon black(CB), silicon carbide (SiC), sodium carboxymethyl cellulose solution (CMC) as raw materials. The effects of sintering atmosphere and carbon black content on the flexural strength, porosity and microstructure of ceramics were investigated. The result shows that: The best sintering atmosphere of the mullite bonded SiC porous ceramic prepared is in coke bed condition; When the content of mullite is 20 % and the content of carbon black is 10 %, the flexural strength of the ceramic is 15 MPa, and the porosity is 42.6 %. At this time, the ceramic has the best performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: DEStech Transactions on Environment, Energy and Earth Sciences
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.