Abstract
The effect of repeated quenching heat treatment on microstructure and dry sliding wear behavior of low carbon PM steel was investigated. For this purpose, atomized iron powder was mixed with 0.3 % graphite and 1 % Ni powders. The mixed powders were cold pressed and sintered at 1200°C for 30 min under pure Ar gas atmosphere. Some of the sintered specimens were intercritically annealed at 760°C and quenched in water (single quenching). The other sintered specimens were first fully austenized at 890°C and water quenched. These specimens were then intercritically annealed at 760°C and re-quenched in water. The martensite volume fraction in the double quenched specimens was higher than that of the single quenched specimen. Wear tests were carried out on the single and double quenched specimens under dry sliding wear condition using a pin-on-disk type machine at constant load and speed. The experimental results showed that the wear coefficient effectively decreased in the double quenched specimen.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.