Abstract
The oxidation behavior of Al-Mg-Sc alloy at 200 °C was investigated. The structure and composition of oxide film on Al-Mg-Sc alloy surface were analyzed by XRD and ARXPS. The microstructure evolution of Al substrate near the interface between Al-Mg-Sc alloy and oxide film was explored by EBSD and TEM. The experimental results indicated that after oxidation treatment at 200 °C, the oxide film was mainly composed of MgO, Al2O3 and a small amount of MgAl2O4. MgAl2O4 was mainly distributed at the bottom of the oxide film and the formation of MgAl2O4 was followed by formation of MgO. Meanwhile, the grains rotated, and part of the LAGBs were transformed into HAGBs with many poorly matched atoms. Mg atoms could quickly diffuse to the grain boundary and the surface through dislocation channels to participate in the oxidation reaction, which favoured the formation of MgAl2O4 at the interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.