Abstract
Zr–Sn–Nb alloy and 304 stainless steel were joined by means of partial transient liquid phase bonding. The effects of Ni interlayer on the microstructure and properties of the joints were investigated. The reaction layers are formed in both joints and which are mainly composed of σ-FeCr layer, Zr(Cr, Fe)2+α-Zr layer and α-Zr+Zr2(Ni, Fe) layer. The intermetallic compounds are compact relatively and cracks are formed in the reaction layer of the direct bonded joint. In the joint with Ni interlayer, many α-Zr phases dispersedly exist in the reaction layer and the thickness of the reaction layer is distinctly larger than that without Ni interlayer. As a result of lower residual stresses and wider crack-free reaction layer, the bonding strength of the joint increases by using Ni interlayer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.