Abstract
Both natural montmorilonite (CN) and organically modified montmorilonite (CB) improved significantly the mechanical performance of novolac phenolic resin (PF)/woven glass-fiber (GF) composites due to their nanodispersion and good interfacial interaction with the matrix. It was revealed that the incorporation of 2.5wt% of the clays enhances the elastic modulus up to 38% for CN and 43% for CB. Aging of PF/GF composites at various aqueous solutions, i.e. water, brine and acidic environments, increased stiffness of the composite (∼100–250% increase in elastic modulus) due to possible secondary crosslinking caused by water molecules and hydroxyl groups of PF resin. However, aging led to the reduction of strength caused by the matrix degradation due to hydrolysis and interfacial debonding. It was found that both clays diminished durability of PF/GF composites probably due to their hydrophilic nature enhancing water absorption.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Composites Part A: Applied Science and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.