Abstract
We report the effect of NaF precursors on the preferential orientation of Cu(In,Ga)Se2 (CIGS) thin films. The CIGS films were grown on NaF/Mo/glass and Mo/glass substrates by using a multi-stage co-evaporation method. The 23-nm-thick NaF precursors were prepared by using an evaporation technique. The CIGS film with a NaF precursor shows a much higher I(112)/I(220/204) XRD peak intensity ratio than the film without it. The (112)- and (220/204)-oriented CIGS films were obtained from highly (0006)- and (30–30)-oriented (In,Ga)2Se3 (IGS) films, respectively. The IGS (0006) orientation was enhanced by the NaF precursor because the lattice misfit of IGS (0006) plane on NaF (−2.3%) was lower than that of IGS (0006) plane on Mo (5.1%) whereas the lattice misfit of IGS (30–30) plane on NaF (1.3%) was higher than that of IGS (30–30) plane on Mo (0.1%). The degree of lattice misfit is believed to play an important role in the preferential growth of CIGS films in the (112) orientation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.