Effect of Molding Method on the Properties of Prepared Quartz Sand Sintered Brick Using the River Sand

Abstract

In order which aim to save land resource and use low grade nature resource to realize high cost performance product. In this paper, the molding method of quartz sand fired brick is discussed. As the plastic (hand pressing) is only used to manually beat the mud mass, the sludge is squeezed by hand. Into the mold and molding and cold isostatic pressure molding pressure of 100 MPa, The difference is far away, which makes the gaps between the particles close to each other greatly different, the pressure of hand-press molding is small, the voids in the blank after molding are large and the hole diameter is large, and the green compact density of the brick body is small. The compact densities of the 65MPa and 150MPa pressed brick bodies are all lower than 100MPa, but 150MPa is still denser than 65MPa. The compressive strength is first increased and then decreased with increasing the molding pressure, when the pressure is 100 MPa, the maximum compressive strength is achieved at 100 MPa achieves the highest point.