Abstract
The effects of spinning conditions on fiber properties are not well explained by the fiber structures because the birefringence, crystallinity, and SAXS patterns are often similar. In this study, the effects on the fiber structure development of polyethylene terephthalate after necking was analyzed by simultaneous WAXD/SAXS measurements. An X-shaped SAXS pattern was observed for all fibers drawn at the minimum draw ratio. In contrast, by drawing under a drawing stress of 100 MPa, the strong diffraction of the smectic phase and an obviously larger long period less than 1 ms after necking were observed for fibers spun at 500–1500 m/min, while almost no smectic phase was observed for fibers spun at 2000 m/min. A higher crystallization rate and clear draw ratio dependence of crystallization rate were also observed for the fiber spun at 2000 m/min. The clear differences in structure development can explain their differences in tensile strength and thermal shrinkage.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.