Abstract
The effect of heat treatment on corrosion properties of CuAlNi shape memory alloy was investigated in 0.9% NaCl solution at pH 7.4 and 37 °C by open circuit potential measurements, polarisation techniques, and electrochemical impedance spectroscopy. Investigations were performed on CuAlNi alloy samples in as-cast state and after heat treatment procedure containing annealing at 850, 885 and 920 °C followed by water quenching. Electrochemical impedance measurement results indicate that heat treatment of CuAlNi alloy leads to the increase in charge transfer resistance and surface layer resistance and the decrease in values of capacitance of the double and surface layers, indicating higher corrosion resistance compared with the as-cast CuAlNi alloy. The increase in polarisation resistance and the decrease in corrosion current density of heat-treated CuAlNi alloy also suggest beneficial influence of heat treatment on corrosion resistance of CuAlNi alloy. Optical microscopy, SEM/EDX and XRD analysis of samples surface after polarisation measurements show the occurrence of pitting corrosion on the electrode surfaces, with the existence of CuCl2, AlCl3 and Cu2Cl(OH)3 compounds as the surface corrosion products.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.