Abstract
In this study the effect of combination of heat treatment of consumable rod and solid solution heat treatment before fast multiple rotation rolling (FMRR) processing on microstructure, mechanical property and wear resistance of Al–Si–Cu alloy friction surfaced on commercial pure aluminum alloy were investigated. Results show that after the FMRR process, there is a significant reduction (99% reduction) in the friction surfaced coating surface roughness. The surface roughness after FMRR processing in the coatings created by homogenized and solid solution treated consumable rod is 0.74 ± 0.12, and 0.56 ± 0.08 μm, respectively. In the coating created by homogenized rod the minimum grain size (1.7 ± 0.2 μm) formed in the FMRR processed layer. Using homogenized consumable rod and FMRR processing by rotational speed of 3000 rpm and traverse speed of 140 mm/min, the maximum hardness (9.8 ± 0.3 GPa) and minimum wear rate (4.6 ± 0.1 μg/m) created at processed layer. FMRR processing by rotational speed of 3000 rpm and traverse speed of 140 mm/min, result in 27 and 24 % increasing in hardness at friction surfaced coating created by homogenized and solid solution treated consumable rods, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.