Abstract
The well-developed plate-like α-Al2O3 particles were obtained by Na2SO4-K2SO4 molten salt synthesis, with diameter range from 8–20 µm and thickness range from 1–2 µm. In order to change the morphology of α-Al2O3 plate-like particles, ferric oxide was added when the sample was prepared. When 10 wt% ferric oxide was added, the phase of sample was still α-Al2O3, but some small plate-like particles were observed, with diameter range from 2–4 µm and the thickness range from 0.1–0.2 µm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.