Abstract
ABSTRACT The present study is carried out to study Glass Fibre Reinforced Aluminium Laminate (GLARE) structures and to evaluate their flexural and tensile properties. The GLARE specimens were fabricated using hand layup with vacuum bag moulding process wherein the aluminium sheets and E-Glass fibre woven mats of fixed thickness are bonded together by application of epoxy resins. Three different thicknesses of aluminium alloy (0.2 mm, 0.3 mm and 0.4 mm) Al-2024 T3 are used for the purpose of the study. The aluminium sheets are stacked together by application of epoxy resin between the sheets and are cured under a compression moulding machine under constant pressure. The overall thickness of the specimen is maintained constant for 2 mm. The samples were subjected to a three-point bending and tensile test as per ASTM D790 and ASTM D3039 standards, respectively, to evaluate their mechanical properties. The results indicate that the tensile strength of the composites is maximum for the specimen with aluminium 2024 T3 face sheet with a minimum thickness of 0.2 mm; however, with the increase in the thickness, the tensile strength is found to be decreasing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.