Effect of double quenching and tempering heat treatment on the microstructure and mechanical properties of a novel 5Cr steel processed by electro-slag casting

Abstract

The effect of double quenching and tempering (DQT) treatment as well as conventional high temperature quenching and tempering (CQT) treatment on the microstructures and mechanical properties of low carbon 5Cr martensitic as cast steel produced by electroslag casting was investigated. The microstructure changes were characterized by optical microscope (OM), scanning electron microscope (SEM), electron back scatter diffraction (EBSD) and transmission electron microscopy (TEM). The characteristics of carbides precipitated during tempering were analyzed on both carbon extraction replica and thin foil samples by TEM. The mechanical performance was evaluated by Vickers hardness test, tensile test, and Charpy V-notch impact test at ambient temperature. The results of microstructure study indicated that DQT treatment led to a finer microstructure than that of CQT. The carbides of the tempered samples were identified as M7C3. The carbides along the prior austenite grain boundaries nucleated directly while those within the laths should be transformed from cementite which formed at the early tempering stage. Compared with CQT condition, yield strength slightly increased after DQT treatment, and impact toughness improved a lot. The strengthening mechanisms were analyzed and it was found that grain refining and precipitation strengthening were mainly responsible for the increase of strength. The superior toughness of DQT condition was attributed to the finer microstructure resulting in more frequent deflections of the cleavage crack and the smaller size of carbides along the prior austenite boundaries. EBSD analysis showed that both martensitic block and packet of low carbon 5Cr tempered martensitic steel could hinder crack propagation, while the latter was more effective.