Abstract
The effect of direct ageing treatment on microstructure and stress-rupture properties of GH761 alloy was studied. Phosphorus was added to the tested alloy for its beneficial effect on stress-rupture life. It was found that the grain size of the tested alloy became much finer after direct ageing treatment, in comparison with the commercial GH761 alloy under standard heat treatment condition. The optimum direct ageing treatment has been determined as follows: 830 degrees C x 4 h, air cooling+720 degrees C x 24 h, air cooling. After such treatment, the higher stress-rupture properties of the test alloy at 650 degrees C, 690 MPa were obtained. The role of phosphorus is still effective under the condition of direct ageing treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.