Abstract
PURPOSEThe purpose of this study was to evaluate the effect of two coloring liquids (aqueous and acid-based coloring liquids) and the position of multilayered zirconia on the flexural strength of multilayered zirconia.MATERIALS AND METHODSThe multilayered zirconia specimens were divided into upper and lower positions. The specimens were divided into three subgroups (n=10): non-shaded, acid-based coloring liquid, and aqueous coloring liquid. The specimens were cut using a milling machine and were immersed in either a acid-based coloring liquid or aqueous coloring liquid 2 times for 5 seconds. The specimens were sintered in a sintering furnace according to the manufacturer's introduction. The flexural strength of the specimen was measured using a universal testing machine and the surface of the specimen was observed using a field emission scanning electron microscope.RESULTSThe flexural strength of multilayered zirconia was 400 – 500 MPa. There was no statistically significant difference among all groups (P>.05).The flexural strength of the multilayered zirconia was not influenced by the kind of coloring liquid used (P>.05). The flexural strength of the multilayered zirconia colored with the coloring liquids was not influenced by its position (P>.05).CONCLUSIONThe different coloring liquid application did not affect the flexural strength of multilayered zirconia of all positions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.