Abstract
The bonded magnet NdFeB has been made by using the hot press method and using Poly Vinyl Butiral (PVB) as a binder. The composition of polymeric binder was varied: 0, 2, 4, 6 and 7 % of weight. Both raw materials are weighed and mixed according to the composition of PVB, then formed by hot press with a pressure 30 MPa, a temperature of 160 ° C and holding time for 30 minutes. The bulk density was measured by using Archimedes method. SEM observation was done to determine the microstructure of bonded magnet NdFeB. The flux magnetic value was measured by using a Gauss meter and the measurement of hysteresis curves was done to know value of remanence Br, coercivity Hc and energy product BHmax by using VSM. According to the characterization results show that the best composition of PVB is 2 of weight. The properties of bonded magnet NdFeB of those compositions are the bulk density around 5.66 g/cm3. Flux Magnetic value: 1862 Gauss, Br value: 5000 kGauss, Hc value: 8.49 kOe and BHmax value : 5.10 MGOe. According of SEM observation results show that the polymer matrix of PVB appears to have covered on all surface grain and filled grain boundary.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.