Abstract

The aim of the work is to study interface formation between Al2O3 particles and Al(Ca) matrix in dependence of Ca content. Aluminium matrix composites (AMC) subjected to investigation were prepared by gas pressure assisted infiltration of alumina beds with aluminium-calcium alloys. It is shown that alumina particles in the AMC are covered with a monocalcium aluminates layer whose coherence increases with increasing amounts of Ca in the aluminium-calcium alloys. Moreover, Al4Ca intermetallic phases are formed with increasing Ca content and interconnect alumina particles. XRD confirms the presence of both CaAl2O4 and CaAl4O7 ternary phases. However, HRTEM analysis confirmed CaAl2O4 with a rather complex structure containing a high density of stacking faults. It appeared that annealing at 735°C does improve consistency of interface for Al 2wt.%Ca/Al2O3 AMC, but do not affect the thickness of the interface in dependence on annealing time.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.