Abstract
The effect of annealing on the changes in the inelastic tunneling contributions in tunneling conductance of ion beam sputtered CoFe/MgO/NiFe magnetic tunnel junctions (MTJs) is investigated. The inelastic contributions are evaluated using hopping conduction model of Glazman and Matveev in the temperature range of 25–300 K. The hopping through number of series of localized states present in the barrier due to structural defects increases from 9 (in as deposited MTJ) to 18 after annealing (at 200 °C/1 h); although no changes in the interface roughness of CoFe-MgO and MgO-NiFe interfaces are observed as revealed by the x-ray reflectance studies on planar MTJs. The bias dependence of tunneling magnetoresistance (TMR) at 25 K is found to get improved after annealing as revealed by the value V1/2 (the bias value at which the TMR reaches to half of its value at nearly zero bias); which is 78 mV (in MTJ annealed at 200 °C/1 h) 2.5 times the value of 33 mV (in as deposited MTJ). At 25 K the inelastic tunneling spectra revealed the presence of zero bias anomaly and magnon excitations in the range of 10–15 mV. While the barrier height exhibited a strong temperature dependence with nearly 100% increase from the value at 300 K to 25 K, the temperature dependence of TMR becomes steep after annealing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.