Abstract
Zinc oxide (ZnO) thin films were deposited on the ordinary glass substrates by spin coating method. The precursor solution was prepared by mixing zinc acetate dehydrate in appropriate proportions with ethanol and diethanolamine (DEA). The obtained thin films were dried at 200°C for 15 minutes in hot air oven. Crystalline ZnO thin films were achieved following annealing process at temperatures 300°, 400° and 500°C for 2 hours. Thin films as- prepared were studied by X-ray diffraction and UV-visible spectroscopy. The films were transparent from near ultraviolet to infrared region. Optical band gap energy of ZnO was obtained 3.22 eV at 300°C. On annealing at 400° and 500°C, band gap energy was shifted at 3.14 eV and 3.05 eV respectively.DOI: http://dx.doi.org/njst.v15i2.12126Nepal Journal of Science and Technology Vol. 15, No.2 (2014) 111-116
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.