Abstract
The effect of annealing conditions on the magnetic characteristics of multilayered perpendicular magnetic tunnel junctions (pMTJs) of the structures SiNx∕Pt∕TbFeCo∕MgO∕(Co∕Pt)5 and SiNx∕Pt∕TbFeCo∕Mg∕MgO∕(Co∕Pt)5 with various MgO barrier thicknesses are explored. We found that both the hard and free layers have coercivity reduction with increasing annealing temperature. However, annealing at median temperature could improve the squareness of the hysteresis loop of the hard layer (TbFeCo). More interestingly, the annealing temperature at which the free layer (Co∕Pt) lost the perpendicular magnetic anisotropy (PMA) depends on the thickness of the MgO layer. Insertion of a thin Mg layer of thickness 0.4nm between the barrier and the hard layer can assist the junction in keeping the PMA at higher annealing temperature. The experimental results suggest that 150°C could be the suitable annealing temperature for these pMTJs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.