Abstract
In order to lower the weight of automotive bodies for better fuel-efficiency and occupant safety, the demand for high Al-containing advanced high strength steel, such as transformation-induced plasticity and twinning-induced plasticity steel, is increasing. However, high aluminum content in steels would tend to significantly affect the properties of mold flux during the continuous casting process. In this paper, a kinetic study of the effect of Al2O3 content on the crystallization behavior of mold flux was conducted by using the single hot thermocouple technique and the Johnson–Mehl–Avrami model combined with the Arrhenius Equation. The results suggested that Al2O3 behaves as an amphoteric oxide in the crystallization process of mold flux. The precipitated phases of mold flux change from cuspidine (Ca4Si2O7F2) into nepheline (NaAlSiO4) and CaF2, and then into gehlenite (Ca2Al2SiO7) with the increase of Al2O3 content. The kinetics study of the isothermal crystallization process indicated that the effective crystallization rate (k) and Avrami exponent (n) also first increased and then decreased with the increase of Al2O3 content. The values for the crystallization activation energy of mold flux with different Al2O3 contents were E R0.8A7 = 150.76 ± 17.89 kJ/mol, E R0.8A20 = 136.43 ± 6.48 kJ/mol, E R0.8A30 = 108.63 ± 12.25 kJ/mol and E R0.8A40 = 116.15 ± 8.17 kJ/mol.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.