Abstract
Effect of Al or Ti addition on the ferrite formation in ultra-low oxygen (about a few tens ppm) weld metal of low carbon steels were investigated. A bead-on-plate welding experiments were performed with a Tungsten Inert Gas (TIG) welding system. The double nozzle was attached to the welding torch used, Ar was passed along the outer nozzle and He is added along the inner nozzle. Optical micrographs showed that primary ferrite appeared along prior austenite grain boundaries and that as the temperature is decreased ferrite side plates were grew into grain interior. Their formation positions were approached to the welding end as the decreasing Al and increasing Ti content. This change in ferrite formation position attributed on the ferrite formation temperature, which was assumed to increase as the decreasing Al and increasing Ti content. Energy dispersive X-ray spectroscopy analysis of inclusions showed that Al and Ti were mainly associated with O, it was obvious that the inclusions in the steels were Al- and Ti- oxide inclusions. Al-oxide inclusions were not favourable acicular ferrite nucleation sites and that the inclusions contributing to acicular ferrite formation were Ti-oxide ones. The number density of acicular ferrite was small. This indicated that acicular ferrite formation was suppressed because the number density of inclusions was low under the ultra-low oxygen welding condition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.