EB‐crosslinked Polymer Electrolyte Membranes Based on Highly Sulfonated Poly(ether ether ketone) and Poly(vinylidene fluoride)/Triallyl Isocyanurate

Abstract

AbstractIn this study, crosslinked polymer electrolyte membranes for polymer electrolyte membrane fuel cell (PEMFC) applications are prepared using electron beam irradiation with a mixture of sulfonated poly(ether ether ketone) (SPEEK), poly(vinylidene fluoride) (PVDF), and triallyl isocyanurate (TAIC) at a dose of 300 kGy. The gel‐fraction of the irradiated SPEEK/PVDF/TAIC (95/4.5/0.5) membrane is 87% while the unirradiated membrane completely dissolves in DMAc solvent. In addition, the water uptake of the irradiated membrane is 221% at 70 °C while that of the unirradiated membrane completely dissolves in water at above 70 °C. The ion exchange capacity and proton conductivity of the crosslinked membrane are 1.57 meq g−1, and 4.0 × 10−2 S cm−1 (at 80 °C and RH 90%), respectively. Furthermore, a morphology study of the membranes is conducted using differential scanning calorimetry and X‐ray diffractometry. The cell performance study with the crosslinked membrane demonstrates that the maximum power density is 518 mW cm−2 at 1036 mA cm−2 and the maximum current density at applied voltage of 0.4 V is 1190 mA cm−2.