Abstract
The dry sliding wear behaviour of different Ti-Nb and Ti-Mo surfaces was investigated in order to evaluate the role of Nb and Mo β-stabilizing elements in titanium wear resistance to consider them for biomedical applications. Dry sliding wear tests were performed under unlubricated conditions using a ball-on-plate tribometer (UMT) with reciprocating lineal movement of 1 Hz frequency at different loads (2 and 5 N) and against two counterface materials (alumina and stainless steel) to assess the effect of these parameters on wear.The results indicated an improvement in wear resistance for all the modified Ti surfaces. Metal-on-metal surfaces exhibited higher wear rate than ceramic-on-metal, and higher wear was observed for the more severe conditions. Wear rate values on modified surfaces were between 53% and 96% lower compared to pure Ti tested at 2 N, and up to 79% lower than Ti at 5 N. In both cases the highest wear reduction was observed for Ti-MoNH4Cl surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.