Abstract
Electrodeposition has attracted tremendous interest in functional coatings due to its advantages of high efficiency, inexpensiveness and ease of implementation. In this work, nickel graphene oxide (Ni-GO), nickel silicon carbide (Ni-SiC) and nickel graphene oxide/silicon carbide (Ni-GO/SiC) composite coatings were electrodeposited on the 2218 aluminum alloy (2218AlA) substrate. The microstructure, microhardness, bonding strength and tribological behaviors of the composite coatings were carried out. According to the results obtained, the composite coatings were dense and compact, with no visible defects and microcracks, and well bonded to 2218AlA substrate. The microhardness of composite coatings was significantly increased compared to that of the 2218AlA substrate. The microhardness of Ni-SiC composite coating was the highest, reaching 3.14 times that of the 2218AlA substrate. The friction response time, friction coefficient and wear rate of the composite coatings were obviously lower. For the Ni-GO composite coating, the average friction coefficient is the smallest at 45.35% of the 2218AlA substrate, while the wear rate is the smallest at 46.97% of the 2218AlA substrate. However, the comprehensive tribological performances of the Ni-GO/SiC composite coating were superior. The abrasive and adhesive wear were the main wear mechanisms of composite coatings, but the degree of damage was different.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.