Abstract
The phosphate glasses of composition Na2O-CaO-P2O5 are widely accepted glass material for biomedical applications. The glass samples with composition (26-x)Na2O-xBaO-29CaO-45P2O5 (x = 0,5,10,15) are prepared at 1100°C by melt-quenching technique. In order to reduce the fast dissolution rate, which limits their application, BaO is added by reducing Na2O composition. The dissolution studies have been carried out in deionized water under semi-dynamic conditions at 37°C for 14 days. The properties are studied based on Barium composition and time of immersion. The samples are taken out at 24 hrs. intervals to carry out weight loss and pH measurements. The rates of cation (Na+ and Ca2+) release from the glass to the solution were found out using flame photometer. The release of orthophosphate (PO43-) anions is measured by UV-Visible spectrometer using phospho-molybdenum blue method. The weight losses linearly increase with time for all the compositions. The addition of barium decreases the weight loss in deionized water. The pH of the solutions varies with dissolution of ions. The dissolution rate has been found out from the slope of the weight loss vs time graph and it decreased with increase in barium content
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.