Abstract
AbstractMicron‐size functional crosslinked poly(methyl methacrylate) (PMMA) particles with narrow size distribution in the range of 1∼5 µm were prepared by dispersion copolymerization in polar media with poly(N‐vinylpyrrolidone)(PVP) as steric stabilizer, 2,2′‐azobisisobutyronitrile(AIBN) as initiator and ethylene glycol dimethylacrylate (EGDMA) as crosslinking agent. The effects of functional comonomer acrylic acid (AA) concentration, contents in AIBN, EGDMA and PVP, media polarity as well as reaction temperature on the particle size and size distribution were investigated. Particle size initially increased, and then decreased with increasing AA concentration in the range of 0.7∼3.5 mol l−1, having a maximum of 5.01 µm at the concentration of 2.1 mol l−1, while size distribution became broader. This was regarded as the result of different roles of PAA in the process. Particle size increased with decreasing media polarity and stabilizer concentration, and with increasing initiator concentration and reaction temperature. The resulting particle shapes were observed by transmission electron microscopy and the presence of carboxyl groups on the surface of the particles was confirmed by Fourier‐transform infrared spectroscopy. Copyright © 2003 Society of Chemical Industry
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.