Abstract
Passivation cracks are studied with experimental observation and finite element simulation. Corner cracks are first initiated, and then edge cracks are subsequently initiated along the edge from the corner to the center. The cracks show a good symmetric pattern over both symmetric axes. Simulation results show that the maximum Von Mises stress is located at die corner, which correlates to the first crack initiation from experimental observation, and the direction of first principal stress matches exactly with the cracking direction (principal stress direction is vertical to the crack surface). Failure criterion for the passivation crack is then discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.