Abstract

For a main chain thermotropic aromatic polyester with a flexible spacer, Cr 194 N 245 I (°C), the director fields around disclinations in the nematic mesophase can be decorated by both the solidification-induced band texture and surface microcracks. Director fields of various types of disclinations, including inversion walls, in the nematic mesophase of this semi-rigid polyester have been observed directly by polarizing optical microscopy. It was found that when the polymer was pre-sheared in the nematic state and then quenched to room temperature, a shear-induced band texture was observed, which relaxed slowly during annealing at 200°C, and then on quenching the solidification-induced band texture and surface microcracks appeared, displaying the pattern of the disclination fields. Pre-shearing is a necessary condition for the appearance of microcracks. On annealing, disclinations of various types were generated, quite often connected by inversion walls in the direction of pre-shearing. In some areas of the specimen where the shear-induced bands had not been completely relaxed during annealing, the shear-induced band texture was shown by the birefringence and surface microcracks to have a supermolecular structure of sinusoidal chain fibrils.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.