Abstract
The need of lead-free ceramics with excellent dielectric behaviors and high energy storage properties have been extensively studied. In this study, (1-x)SrTiO3-x(0.94Bi0.54Na0.46TiO3-0.06BaTiO3) ((1-x)ST-xBNBT) lead-free ceramics were designed and fabricated using the conventional solid state sintering method. The results demonstrate that the dielectric constant of (1-x)ST-xBNBT ceramics increases gradually and reaches the maximum value (∼3940) with x = 0.6 at 100 Hz, which is 11.94 times as large as that of pure SrTiO3 (∼330), and the dielectric loss is lower than 0.20 at the measured frequencies for all the samples. Meanwhile, the dielectric measurements reveal an intensified diffusion and relaxor behavior. All the samples show slim polarization-electric field (P-E) loops, and the optimal recoverable energy storage density (Wrec) of 1.88 J/cm3 together with high energy storage efficiency (η) of 79% can be achieved with x = 0.5, which indicates that the (1-x)ST-xBNBT ceramics may be promising lead-free ceramics for high energy storage applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.