Abstract
Recently, a new additive for grain refinement of Ni based superalloys has been developed. In those studies, it was considered that niobium carbide in Ni–Nb–C alloy additives would act as nuclei on the solidification of Ni based superalloys. It is known that the crystallographic characteristics of iron are quite similar to those of nickel. Thus, it was expected that niobium carbide would act as a grain refiner for iron base alloys, especially for austenitic steels. In this study, the effect of the additives on the microstructure of SUS316 steel was examined in various experimental conditions. The grain size of SUS316 specimens without inoculation was ∼2700 μm. On the other hand, when NbC containing alloy additives were added into the SUS316 melt, fine equiaxed grains were observed and the grain size of the specimen was significantly reduced to ∼200 μm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.