Abstract
This research aims to develop a multiphase steel combining spheroidal cementite and bainite in ductile ferrite matrix possessing an optimal balance of reasonably high strength and excellent ductility. A high carbon (0.61 wt.%) high silicon (1.71 wt.%) EN45 spring steel was annealed to obtain ferrite pearlite microstructure. The samples were given 5 and 10% cold rolling followed by holding at temperature below Ac1 for about 3 h. The samples were then held in intercritical range at 770 °C temperature for different durations ranging from 5 to 20 min for partial re-austenitization followed by quenching in a salt bath maintained at 350 °C and holding for 10 min to get bainite. The samples were finally water quenched. Characterizations of the samples with the help of optical microscopy, x-ray diffraction, scanning electron microscopy, and atomic force microscopy were carried out. Optimal heat-treatment conditions were found out after correlating with tensile properties. The best combination of high tensile strength (~800 MPa) with very high elongation (~29%) was obtained. Effects of cold-rolled strain and holding time in the intercritical region on the mechanical properties and microstructural changes were studied. Finally, structural property correlation is established.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.