Abstract
This work uses high-energy synchrotron X-ray diffraction (HEXRD), atomic force microscope (AFM), nanoindentation and EBSD technology to explore a new method for measuring residual stress in strong R {124} 〈211〉 texture alloys, and the distribution of residual stress and Young's modulus in different crystal orientations. Compared with the traditional Voigt and Reuss model, for the textured Cu-Ni-Si-Co alloy, a local Voigt and Reuss inter-grain interaction model based on HEXRD diffraction technology is established, which can more accurately characterize the residual stress of superficial layer (230 μm). The local stress model provides a new X-ray diffraction method for testing the residual stress of textured materials. Aiming at the textured Cu-Ni-Si-Co alloy with compressive stress, the quasi-in-situ method combining EBSD and nanoindentation is used to characterize the residual stress of different crystal orientations in the microdomain. The hard orientation [111] grain direction has the highest residual stress, and the soft orientation [100] grain direction has the lowest residual stress, and the residual compressive stress in the hard orientation is about twice that of the soft orientation. In addition, the Young's modulus of the material is also the largest on [111] hard-oriented grains and the smallest on [100] soft-oriented grains.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.