Design of low surface roughness-low residual stress-high optoelectronic merit a-IZO thin films for flexible OLEDs

Abstract

The development of efficient and reliable large-area flexible optoelectronic devices demands low surface roughness-low residual stress-high optoelectronic merit transparent conducting oxide (TCO) thin films. Here, we correlate surface roughness-residual stress-optoelectronic properties of sputtered amorphous indium zinc oxide (a-IZO) thin films using a statistical design of experiment (DOE) approach and find a common growth space to achieve a smooth surface in a stress-free and high optoelectronic merit a-IZO thin film. The sputtering power, growth pressure, oxygen partial pressure, and RF/(RF+DC) are varied in a two-level system with a full factorial design, and results are used to deconvolve the complex growth space, identifying significant control growth parameters and their possible interactions. The surface roughness of a-IZO thin film varies over 0.19 nm to 3.97 nm, which is not in line with the general assumption of low surface roughness in a-IZO thin films. The initial regression model and analysis of variance reveal no single optimum growth sub-space to achieve low surface roughness (≤0.5 nm), low residual stress (−1 to 0 GPa), and industrially acceptable electrical conductivity (>1000 S/cm) for a-IZO thin films. The extrapolation of growth parameters in light of the current results and previous knowledge leads to a new sub-space, resulting in a low residual stress of −0.52±0.04 GPa, a low surface roughness of 0.55±0.03 nm, and moderate electrical conductivity of 1962±3.84 S/cm in a-IZO thin films. These results demonstrate the utility of the DOE approach to multi-parameter optimization, which provides an important tool for the development of flexible TCOs for the next-generation flexible organic light emitting diodes applications.