Abstract

Transmission electron microscopy was used to investigate the coexistence of ferroelectricity (FE) and antiferroelectricity (AFE) in (001) and (011) (Pb0.97, La0.02) (Zr0.95, Ti0.05) O3 (PLZT) epitaxial thin films. The depth resolved selected area electron diffraction (SAED) results revealed that the AFE phase was located in the near interface region, whereas the FE phase was found in the near surface region. A thickness dependent lattice parameter distribution was calculated using the SAED data, and a decrease in the c/a ratio was found to correlate with the transition from AFE to FE stability. Additionally, commensurate and incommensurate modulations in AFE PLZT were identified based on the observation of various superlattice reflections.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.