Abstract
AbstractLithium metal is the best candidate anode for high specific energy density batteries because of its high specific capacity and low negative potential. However, lithium dendrite formation and growth during the lithium plating and stripping cycles have hindered the use of lithium metal as the anode for practical batteries. Here, a mechanism for the suppression of lithium dendrite formation and growth in a composite separator of Kimwipe paper (KW) and porous polyethylene (PE) for various electrolytes was examined. The Li/KW/PE electrode in an electrolyte of 1 m Li(CFSO3)2N (LiFSI) in 1,4, dioxane (DX)‐1,2 dimethoylethane (DME) (1 : 2 v/v) with a wide electrochemical window was successfully cycled without lithium dendrite short‐circuiting at 5 mA cm−2 and 25 °C for 10 h over 25 cycles. Lithium was deposited into the cellulose fiber network during the lithium plating process, which resulted in the formation of a three‐dimensional (3D) lithium electrode. Whereas, the composite separator of KW and PE was not effective to suppress the lithium dendrite formation and growth with the conventional carbonate based electrolyte of 1 m LiPF6 in ethylene carbonate‐dimethyl carbonate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.