Abstract
Although fly ash has been widely used in concrete as a cement replacement, little work has been done on determining the degree of hydration of high-volume fly ash/cement (FC) systems. In the present study, the degree of hydration of the cement in Portland cement (PC) paste was obtained by determining the non-evaporable water (Wn) content. The degree of reaction of the fly ash in FC pastes was determined using a selective dissolution method. Based on the relation between the degree of cement hydration and effective water-to-cement (w/c) ratio, the degree of hydration of the cement in FC pastes was also estimated. It was found that high-volume fly ash pastes underwent a lower degree of fly ash reaction, and in the pastes with 45% to 55% fly ash, more than 80% of the fly ash still remained unreacted after 90 days of curing while the hydration of the cement in high-volume fly ash pastes was enhanced because of the higher effective w/c ratio for the paste. This effect was more significant for the pastes with lower water-to-binder (w/b) ratios. Thus, preparing high-volume fly ash concrete at lower w/b ratios can result in less strength losses. This paper also introduces a model to describe the relationship between the w/c ratio and the degree of cement hydration and gel/space ratio. The gel/space ratios of the FC pastes, evaluated based on the proposed model, were found to be consistent with the gel/space ratio of PC pastes in terms of the relationship with compressive strength. The gel/space ratio data correlated (inversely) linearly with mercury intruded porosity, but the former correlated more with compressive strength than the latter.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.