Abstract
This study examined the effect of heat-treatment and multi-coating on the microstructure and optical properties of photonic crystals (PCs) that had been self-assembled using mono-dispersed spherical SiO2 nanoparticles. When the heat-treatment temperature was increased, the reflectance peak due to the photonic bandgap moved to a shorter wavelength direction, and the peak intensity of the Fabry-Perot fringes increased. The highest reflectance peak intensity was obtained in the sample heat-treated at 250-300 degrees C. Heat-treatment reduced the average particle size and number of defects, and increased the packing density of the PC. When the heat-treatment temperatures were increased up to 900 degrees C, a large crack with an average size of approximately 1.3 microm was formed through the self-assembled layer. A multi-coating could effectively fill the open space of this crack and thereby reduce the total number of defects. The crystallinity and optical properties of the self-assembled PC were improved by the heat-treatment and multi-coating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.